Industrial Laminated Sheets & Rods:
|
Units
|
E-P1
|
E-P2
|
E-P3
|
Tensile Strength (min)
|
kgf/cm2
|
850
|
720
|
550
|
Flexural Strength (min)
|
kgf/cm2 |
1340
|
1340
|
860
|
| Shear Strength (min) |
kgf/cm2 |
765
|
715
|
620
|
| Impact Strength (min) |
kgf/cm2 |
4.10
|
3.05
|
2.00
|
| Compression Strength (min) |
kgf/cm2 |
860
|
860
|
860
|
| Electrical Strength (Proof voltage) |
|
|
|
|
a. Flatwise (for 1.6 mm thickness)
|
kv
|
-
|
15
|
15
|
b. edgewise
|
kv
|
-
|
15
|
20
|
Insulation Resistance (min.)
|
M
|
1
|
54
|
1000
|
Water Absorption of 1.6 mm (max.)
|
mg
|
220
|
150
|
35
|
Power Factor (tan) at 1 MHz
|
-
|
-
|
|
0.045
|
Permittivity at 1 MHz
|
-
|
-
|
|
5.8
|
Thickness (Range) Available
|
mm
|
0.8 to 50.0
|
0.8 to 50.0 |
0.8 to 50.0 |
Punchability(Maximum thickness limit)
|
|
Hot 2.5 mm
|
Hot 2.5 mm |
Hot 2.5 mm |
|
Units
|
E - F2
|
E-F3
|
Tensile Strength (min.)
|
Kgf/cm2
|
620
|
540
|
Flexural Strenght (min.)
|
Kgf/cm2 |
1060
|
950
|
Shear Strength (min.)
|
Kgf/cm2 |
530
|
520
|
| Impact Strength (min.) |
Kgf/cm2 |
9.3
|
11.3
|
| Compression Strength (min.) |
Kgf/cm2 |
820
|
820
|
| Electrical Strength (Proof Voltage) |
|
|
|
a. Flatwise (for 1.6 mm thickness)
|
kv
|
1
|
1
|
b. edgewise
|
kv
|
1
|
1
|
Insulation Resistance (min.)
|
M
|
1
|
0.5
|
Water Absorption of 1.6 mm (max.)
|
mg
|
70
|
70
|
Thickness (Range) Available
|
mm
|
0.5 to 100.0
|
0.5 to 100.0
|
Punchability (upto 2.5 mm)
|
Cold Punching
|
|